UPS 19003 THISTLEBOND A&B CEMENT is a high performance, two pack, solvent free epoxy repair system for use on metallic surfaces. The product is ideal for application where only minimal surface preparation can be carried out and is usually used in conjunction with UPS 19000 RH.
Solvent free epoxy repair cement / paste – 1:1 mixing ratio
No shrinkage
Outstanding adhesion to manually prepared surfaces
Excellent chemical resistance
High compressive strength
Can be over coating with epoxy & polyurethane coatings and repair materials
Formally known as TRK 19002/3
Typically, the material is used in conjunction with UPS Composite Repair Systems as a cost-effective surface filler prior to application of UPS 19000 RH and UPS 19007/9 GT. The material can also be used for;
Seal leaking tank seams
Filling of pitting and scarring on badly corroded or eroded metallic surfaces
Cold bond steel plates to leaking tanks and pipes
Surface Preparation Manual | Mechanical
Lighting Loading
6 hours
Spatula or Applicator Tool Applied
Cost Effect Solution
Useable Life
30 minutes @ 20°C (68°F)
Compressive Strength
(ASTM D695)
735KG/cm² (10.450 psi)
Pull Off Adhesion
(ASTM D4541 Abrasive Blasted Mild Steel with 75 micron profile)
244KG/cm² (3,480 psi)
Manually Prepared Steel Plate
115KG/cm² (1,640 psi)
Movement Without Load or Immersion
2 hours @ 20°C (68°F)
Compressive Strength
(ASTM D695)
1,034KG/cm² (14,700 psi)
Corrosion Resistance
(ASTM B117)
Minimum 5,000 hours
Pack Sizes
200GM (0.44LB) | 1KG (2.2LB) | 3KG (6.6LB)
1KG (2.2LB) of fully mixed product will give the following coverage rates -
0.625m² at 1mm
6.7ft² at 40mil
Please note that the coverage rates quoted are theoretical and don't take into consideration the profile or condition of the surface being repaired
Suitable for long-term water immersion at temperatures up to 70°C (158°F)
Resistant to dry heat in excess of 150°C (302°F) dependent on load