UPS 407 EN EPOXY NOVOLAC is a high build solvent free epoxy novolac coating. Designed to provide outstanding chemical and corrosion protection of steel and concrete structures.
The coating is particular resistant to attack by strong acids including 98% sulphuric acid.
Excellent adhesion to correctly prepared surfaces
Outstanding chemical resistance to a wide range of industrial chemicals
Brush, Roller, Standard Airless spray applied
Application and cure at room temperature –
No hot work necessary
Excellent resistance to abrasion and mechanical damage
Resistant to 98% Sulphuric Acid & 36% Hydrochloric Acid in immersion conditions
Solvent free –
Reducing Health & Safety concerns
Formally known as Chemi-Tech UC / 175 UC
Applications for UPS 407 EN EPOXY NOVOLAC include:
Chemical resistant coating for bunds, secondary containments, chemical spill areas, tank plinths etc.,
Protection of pumps, valves fittings etc.,
Chemical drains, channels and sumps
Protection of concrete areas subject to aggressive chemicals – Pump bases
Airless Spray Applied
Brush Applied
Roller Applied
Wet Heat Resistance up to 60°C (120°F)
Useable Life
25 mins @ 20°C (68°F)
Water / Sea Water Immersion
4 days @ 20°C (68°F)
Abrasion Resistance
(Taber CS17 Wheels / 1KG Load)
138mg loss / 1000 cycles
0.18cc loss / 1000 cycles
Available Colours
Grey | Red
Minimum Over-Coating Window
4 hours @ 20°C (68°F)
Tensile Shear Adhesion
(ASTM D1002 Abrasive Blasted Mild Steel with 75-micron profile)
208KG/cm² (2,950 psi)
Heat Distortion
(ASTM D648 at 264psi fibre stress)
20°C Cure – 52°C
100°C Cure – 75°C
Pack Sizes
4LTR (1.1 US Gallon) | 16LTR (4.2 US Gallon)
4LTR (1.1 US Gallon) of fully mixed product will give the following coverage rates -
10m² at 400 microns 107ft² at 16mil
8m² at 500 microns 85ft² at 20mil
16LTR (4.2 US Gallon) of fully mixed product will give the following coverage rates -
37.5m² at 400 microns 402ft² at 16mil
32m² at 500 microns 343ft² at 20mil
Please note that the coverage rates quoted are theoretical and do not take into consideration the profile or condition of the surface being repaired
Suitable for use in immersed conditions at temperatures up to 60°C (120°F) dependent on chemical contact
Dry conditions up to 200°C (392°F) dependent on load
The product demonstrates resistance to a wide variety of inorganic acids, alkalis’, salts and organic media
Chemical
Sulphuric Acid
Acetic Acid
Ammonia Hydroxide
Chromic Acid
De-ionised Water
Hydrobromic Acid
Hydrocholric Acid
Benzene
Phosphoric Acid
Butanol
Nitric Acid
Ammonia Hydroxide
Ethanol
Toluene
Xylene
Concentration
98%
10%
30%
10%
-
40%
36%
100%
75%
100%
10%
30%
100%
100%
100%
Temperature
40°C (104°F)
30°C (86°F)
45°C (113°F)
40°C (104°F)
40°C (104°F)
30°C (86°F)
35°C (95°F)
35°C (95°F)
45°C (113°F)
40°C (104°F)
30°C (86°F)
45°C (113°F)
45°C (113°F)
40°C (104°F)
40°C (104°F)
If the chemical is not listed, please refer to the Unique Polymer Systems Technical Centre for advice
Email: sales@uniquepolymersystems.com or call +44 (0) 1531 636 300