APPLICATION INSTRUCTIONS |
SAFETY
PRECAUTION
Before opening or working
with Fluorolast products, please refer to the MSDS for safety information.
|
SURFACE
PREPARATION
Prepare surfaces according to these guidelines. STEEL
SURFACES: Before sandblasting, remove all traces of oil and grease using
a suitable detergent, followed by a clean-water washing. All steel surfaces
should be sandblasted to white metal in accordance with NACE specification
#1. CONCRETE SURFACES: New surfaces must age at least 28 days. All construction
dust and loose contaminants, etc., must be removed. Old surfaces should
be cleaned to remove any surface contaminants such as stains, previous
coatings, etc. A hydroblast or sandblast is highly recommended. OTHER
SURFACES: All materials (rubber, plastic, wood, fabric, etc.) should be
clean and free of surface contaminants. Contact our Coatings Research
laboratory for more information. |
DIRECTIONS
FOR USE
Fluorolast WB-200 Series is a two-component, water-borne
room temperature-curable coating. Add the catalyst and mix thoroughly.
The catalyzed coating has a potlife of 12 to 24 hours. If necessary, the
coating may be thinned with distilled water. The CA-75 catalyst is provided
in the correct amount for the coating. |
|
top of
page |
APPLICATION
METHODS
4 mil minimum dry film thickness (dependent on severity
of application). |
| |
|
|
| |
SPRAYING:
|
1-2 mils wet
film thickness using any conventional air atomizing spray gun. Can
be used with gravity, pressure or suction feed supply. |
| |
|
PSI in line:
38 |
| |
|
PSI in canister:
18 |
| |
FLUID TIP
SIZE: |
16oz./min
.034" (.85mm) |
| |
|
20oz./min. .042"
|
| |
|
30oz./min.
.055" |
| |
DIPPING:
|
1-2
mils Dry Film Thickness (DFT). Immerse part in coating, remove slowly
and allow to dry. |
|
top of
page |
MULTIPLE
COATS APPLICATION
Apply multiple coats to obtain the total DTF that
you desire. Coating should be dry to touch before applying another coat
(approximately 20 minutes). |
CURING
The catalyzed coating will cure in approximately
72 hours at 70° F and 50% RH. |
COATING
STORAGE
The uncatalyzed coating may be stored for 3 months
at 50° to 72° F. To ensure a 3 month shelf life, the uncatalyzed
coating must be stirred or agitated once a week. |
CLEANUP
PROCEDURE
Use warm water and a suitable detergent for washing
followed by a thorough warm water rinse.
|
|
top of
page |
|
| TECHNICAL
DATA |
|
PHYSICAL PROPERTIES AND
TYPICAL VALUE CHART |
|
|
|
|
|
Stock Colors
|
|
|
2
|
|
|
100
|
|
|
53
|
|
|
65
|
|
|
1
|
|
|
810
|
- Continuous Operating Temp., °F
|
-40 to 400
|
|
|
Up to 1500
|
|
|
Up to 600
|
|
|
Excellent
(0.11g/1000 cycles H-22 wheel, 1000g
load)
|
- Adhesion ASTM D-4541
(Carbon Steel NACE #2), PSI
|
>1000
|
|
|
Approximately 20 min.
@ 70° F, 50% RH
|
|
|
Approximately 4 - 6 days
@ 70° F, 50% RH
|
|
|
top of
page
|
|